| Spring Steel Strip Out Of 1.4369 (X11CrNiMnN19-8-6) (EN 10151 – 1.4369) |
|||||||||||||||
| Composition |
|||||||||||||||
| Element |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
N |
|||||||
| Mass [%] min. |
0.07 |
0.50 |
5.0 |
17.5 |
6.5 |
0.2 |
|||||||||
| Mass [%] max. |
0.15 |
1.00 |
7.5 |
0.030 |
0.015 |
19.5 |
8.5 |
0.3 |
|||||||
| Dimensional range |
|||||||||||||||
| 0.05 mm ≤ d ≤ 3.00 mm b ≤ 600 mm |
|||||||||||||||
| Mechanical technological properties |
|||||||||||||||
Modulus of elasticity E in [GPa] |
200 |
Density in [kg/dm³] |
7.90 |
||||||||||||
| The modulus of elasticity E is dependent on the material treatment and working temperature. The tensile strength is divided into classes. Further properties: see EN 10151 |
|||||||||||||||
| Application |
|||||||||||||||
| This material is chosen for stainless springs, if they have to be definitely non-magnetic. These springs can be used in high working temperatures up to 250 °C. Compared to 1.4310, this material reaches a slightly lower cold hardening point. This material is normally not used in the SCHERDEL Group. |
|||||||||||||||
| Special treatment |
|||||||||||||||
| none |
|||||||||||||||